- Title:
-
Effect of Ga on electrochemical corrosion behavior of Fe40Ni40P14B6 amorphous alloy
- Author(s):
-
LI Fushan; Du Xueshan; Ren Chenxing; etc
-
-
- Keywords:
-
- CLC:
-
-
- DOI:
-
10.3969/j.issn.1671-6833.2004.03.019
- Abstract:
-
Fe-based amorphous alloy (Fe40Ni40P14B6) with high glass formation capacity 100-xGax (x=0, 2.5 and 4.5) was prepared by single-roller copper wheel rotation. The corrosion behavior of amorphous alloy (Fe40Ni40P14B6) 100-xGax (x=0, 2.5 and 4.5) in HCl solution of 1 mol/L and 3 mol/L was studied by electrochemical method, and the results showed that the amorphous alloy (Fe40Ni40P14B6) 100-xGax (x=0, 2.5 and 4.5) had high corrosion characteristics in HCl solution, and the corrosion resistance of iron-based amorphous alloy increased with the increase of Ga content. In addition, the corrosion resistance of amorphous alloy (Fe40Ni40P14B6) 100-xGax (x=0, 2.5 and 4.5) and stainless steel (1Cr18Ni9Ti) in HCl solution of 1 mol/L and 3 mol/L respectively, the corrosion resistance of amorphous alloy is better.