[1]张效宁,宋杰,范志国..Beta Ti-9.8Mo-3.9Nb-2V-3.1Al合金的热压缩变形行为研究[J].郑州大学学报(工学版),2009,30(01):10-13.[doi:10.3969/j.issn.1671-6833.2009.01.003]
ZHANG Xiaoning,SONG Jie,Fan Zhiguo.Study on hot compression set behavior of Beta Ti-9.8Mo-3.9Nb-2V-3.1Al alloy[J].Journal of Zhengzhou University (Engineering Science),2009,30(01):10-13.[doi:10.3969/j.issn.1671-6833.2009.01.003]
点击复制
Beta Ti-9.8Mo-3.9Nb-2V-3.1Al合金的热压缩变形行为研究(
)
《郑州大学学报(工学版)》[ISSN:1671-6833/CN:41-1339/T]
- 卷:
-
30卷
- 期数:
-
2009年01期
- 页码:
-
10-13
- 栏目:
-
- 出版日期:
-
1900-01-01
文章信息/Info
- Title:
-
Study on hot compression set behavior of Beta Ti-9.8Mo-3.9Nb-2V-3.1Al alloy
- 作者:
-
张效宁; 宋杰; 范志国.
-
上海交通大学,材料科学与工程学院,上海,200240, 上海交通大学,材料科学与工程学院,上海,200240, 上海交通大学,材料科学与工程学院,上海,200240
- Author(s):
-
ZHANG Xiaoning; SONG Jie; Fan Zhiguo
-
Shanghai Jiao Tong University, School of Materials Science and Engineering, Shanghai, 200240, Shanghai Jiao Tong University, School of Materials Science and Engineering, Shanghai, 200240, Shanghai Jiao Tong University, School of Materials Science and Engineering, Shanghai, 200240
-
- 关键词:
-
Ti-Mo合金; 热压缩变形; 析出相
- Keywords:
-
Ti-Mo alloy; hot compression deformation; Precipitated phase
- DOI:
-
10.3969/j.issn.1671-6833.2009.01.003
- 文献标志码:
-
A
- 摘要:
-
采用Gleeble-3500热模拟机对Ti-9.8Mo-3.9Nb-2V-3.1Al合金进行了室温～800 ℃范围内的热压缩变形试验,应变速率0.1 s-1.结果显示,在室温～300 ℃和500～800 ℃范围内,合金的变形抗力随温度的升高而降低,但是在300～500 ℃出现了异常的变形抗力随温度升高而升高的现象.最后讨论了热压缩变形行为对于试验结果的影响.
- Abstract:
-
Gleeble-3500 thermal simulator was used to test the hot compression set test of Ti-9.8Mo-3.9Nb-2V-3.1Al alloy in the range of room temperature ~ 800 °C, and the strain rate was 0.1 s-1. The results showed that in the range of room temperature ~ 300 °C and 500 ~ 800 °C, the deformation resistance of the alloy decreased with the increase of temperature, but at 300~500 °C, abnormal deformation resistance increased with the increase of temperature. Finally, the influence of thermal compression set behavior on the experimental results is discussed.