灰口铸铁与碳钢耐酸腐蚀研究(
)
《郑州大学学报(工学版)》[ISSN:1671-6833/CN:41-1339/T]
- 卷:
-
2
- 期数:
-
1981年01期
- 页码:
-
47-53
- 栏目:
-
- 出版日期:
-
1981-06-18
文章信息/Info
- Title:
-
Study on acid corrosion resistance of gray cast iron and carbon steel
- 作者:
-
楼南金
-
郑州工学院实习工厂,
- Author(s):
-
Lou Nanjin
-
Zhengzhou Institute of Technology internship factory,
-
- Keywords:
-
In this paper; boronitriding; a method of chemical heat treatment; was used to change the chemical composition of the surface layer of carbon steel and cast iron; improve the structure of the surface layer and increase the electrode potential; so as to obtain the acid-resistant corrosion layer.Through a series of heat treatment process; acid corrosion resistance test and metallographic analysis; the best boronitriding agent formulation and treatment process were determined.When the flake graphite size of gray cast iron is less than grade 4; the acid corrosion resistance of gray cast iron can be significantly improved by boronitriding.Ordinary carbon steel after treatment; at room temperature; can withstand different concentrations of hydrochloric acid; sulfuric acid corrosion.Therefore; under appropriate conditions; it can be used to replace some stainless steel and save the rare nickel-chromium alloy.
- 文献标志码:
-
A
- 摘要:
-
本文通过化学热处理的方法——硼氮共渗,来改变碳钢与铸铁表层的化学成份,改善表层的组织结构和提高电极电位,从而获得耐酸腐蚀层。通过一系列热处理工艺,耐酸腐蚀试验和金相分析,确定了最佳的硼氮共渗剂配方及处理工艺。灰口铸铁的片状石墨尺寸小于四级时,硼氮共渗可显著提高其耐酸腐蚀性能;普通碳钢处理后,在常温下,能承受不同浓度的盐酸、硫酸的腐蚀。因此,在适当条件下,可用它来代替部分不锈钢,节约稀贵的镍铬合金.